Sabic Lexan PC EXL1414-NA8A005T
2016-11-14 09:20
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 |
比重
|
ASTM D792, ISO 1183 | 1.19 |
g/cm³
|
|
| 熔流率 | 300℃/1.2 kg | ASTM D1238 | 10 |
g/10 min
|
|
| 溶化體積流率 | 300℃/1.2 kg | ISO 1133 | 9.50 |
cm³/10min
|
|
| 收縮率 | 流動3.20 mm | Internal Method |
0.40 到 0.80
|
% | |
|
橫向流動: 3.20 mm
|
Internal Method |
0.40 到 0.80
|
% | ||
|
吸水率
|
飽和, 23℃
|
ISO 62 | 0.12 | % | |
|
平衡, 23℃, 50% RH
|
ISO 62 | 0.093 | % | ||
| 洛氏硬度 | L 計秤 | ISO 2039-2 | 87 | ||
| 機械性能 |
拉伸模量
|
-- | ASTM D638 | 2190 |
MPa
|
| -- | ISO 527-2/1 | 2310 |
MPa
|
||
|
抗張強度
|
屈服 | ASTM D638 | 57.6 |
MPa
|
|
| 屈服 | ISO 527-2/50 | 56.8 |
MPa
|
||
| 斷裂 | ASTM D638 | 59.1 |
MPa
|
||
| 斷裂 | ISO 527-2/50 | 55.3 |
MPa
|
||
|
伸長率
|
屈服 | ASTM D638 | 5.6 | % | |
| 屈服 | ISO 527-2/50 | 5.4 | % | ||
| 斷裂 | ASTM D638 | 120 | % | ||
| 斷裂 | ISO 527-2/50 | 110 | % | ||
|
彎曲模量
|
50.0 mm 跨距 | ASTM D790 | 2180 |
MPa
|
|
| -- | ISO 178 | 2120 |
MPa
|
||
|
彎曲強度
|
-- | ISO 178 | 88.6 |
MPa
|
|
| 屈服, 50.0 mm 跨距 | ASTM D790 | 92.0 |
MPa
|
||
|
簡支梁缺口沖擊強度
|
-30℃ | ISO 179/1eA | 60 |
kJ/m²
|
|
| 23℃ | ISO 179/1eA | 70 |
kJ/m²
|
||
| 簡支梁缺口沖擊強度 | -30℃ | ISO 179/1eU |
無斷裂
|
||
| 23℃ | ISO 179/1eU |
無斷裂
|
|||
|
懸壁梁缺口沖擊強度
|
-30℃ | ASTM D256 | 710 |
J/m
|
|
| 23℃ | ASTM D256 | 820 |
J/m
|
||
| -30℃ | ISO 180/1A | 55 |
kJ/m²
|
||
| 23℃ | ISO 180/1A | 65 |
kJ/m²
|
||
| 無缺口伊佐德沖擊強度 | -30℃ | ISO 180/1U |
無斷裂
|
||
| 23℃ | ISO 180/1U |
無斷裂
|
|||
| 裝有測量儀表的落鏢沖擊 |
-30°C, Total Energy
|
ASTM D3763 | 77.4 | J | |
| 23℃, Total Energy | ASTM D3763 | 75.5 | J | ||
| 熱性能 |
熱變形溫度
|
1.8 MPa, 未退火, 3.20 mm
|
ASTM D648 | 121 | ℃ |
|
1.8 MPa, 未退火, 6.40 mm
|
ASTM D648 | 116 | ℃ | ||
|
維卡軟化溫度
|
-- | ASTM D1525.ISO 306/B50 | 139 | ℃ | |
| -- | ISO 306/B120 | 138 | ℃ | ||
| Ball Pressure Test | 125℃ | IEC 60695-10-2 |
Pass
|
||
|
線形膨脹系數
|
流動: -40 到 40℃ | ASTM E831 | 0.000067 | cm/cm/℃ | |
|
流動: 23 到 80℃
|
ISO 11359-2 | 0.000067 | cm/cm/℃ | ||
| 橫向: -40 到 40℃ | ASTM E831 | 0.000080 | cm/cm/℃ | ||
|
橫向: 23 到 80℃
|
ISO 11359-2 | 0.000080 | cm/cm/℃ | ||
|
RTI Elec
|
UL 746 | 130 | ℃ | ||
|
RTI Str
|
UL 746 | 130 | ℃ | ||
| 電氣性能 |
表面電阻率
|
IEC 60093 |
> 1.0E+15
|
ohm
|
|
|
體積電阻率
|
IEC 60093 |
> 1.0E+15
|
ohm·cm
|
||
| 可燃性 |
UL 阻燃等級
|
0.800 mm
|
UL 94 |
HB
|
|
|
3.00 mm
|
UL 94 |
V-2
|
|||
|
灼熱絲易燃指數
|
3.00 mm | IEC 60695-2-12 | 960 | ℃ | |
|
熱燈絲點火溫度
|
0.800 mm
|
IEC 60695-2-13 | 850 | ℃ | |
|
3.00 mm
|
IEC 60695-2-13 | 850 | ℃ | ||
| 光學性能 | 透射率 | 2540 µm | ASTM D1003 | 82.0 | % |
| 霧度 | 2540 µm | ASTM D1003 | 3.0 | % | |